The determination of particle size distribution is an important parameter for controlling industrial processes, particularly in the field of pharmaceuticals. It is also an important parameter for characterizing nanoparticles. The best technique for determining particle size distribution is scanning electron microscopy. The process of counting particles is typically performed manually, which requires both more time and a higher standard deviation than automatic methods. This study shows the results of a particle counting procedure that relies on a fully automated method that was found to improve the reproducibility of the measurement. The effect on the diameter of near-spherical polymer nanospheres between 20 and 100 nm (mean of 60 nm) when samples were coated by a conducting layer (such as gold or carbon) was also evaluated. The images were collected using a field emission scanning electron microscope and then processed using the ImageJ program. Results showed that the method proposed in this work produces mean diameter values in accordance with NIST-traceable near-spherical polymer nanospheres for the sample without coating. The study also revealed two main effects of the conductive coating: changes to topography and an increase in mean particle diameter.

The present paper describes the nonohmic behavior of the SnO2.MnO-based system and analyzes the influence of the sintering time and the Nb2O5 concentration on this system's electrical properties. A nonlinear coefficient of ~7 was obtained for a 0.2 mol%-doped Nb2O5 composition, which is comparable to other values reported in the literature for the ternary SnO2-based systems. A recent barrier formation model proposed in the literature to explain the nonlinear electrical behavior of SnO2-based systems is used to clarify the role of the MnO constituent in the formation of the barrier, taking into account the influence of segregated atoms, precipitated phase and oxygen species in the grain boundary region.